Dental Model Pro Grey
1 000,00 zł
Liqcreate Dental Model Pro Grey is a matte, opaque grey colored photopolymer. Its matte surface finish accentuates depth and detail in dental models, which accommodates a perfect view on undercuts and the surface is ideal for scan impressions. 3D-printed parts from this material have exceptional dimensional stability and low shrinkage during printing.
Liqcreate Dental Model Pro Grey is easy to use on open SLA, MSLA and DLP 3D-printers in the range of 385 – 420nm. This material has excellent properties like low shrinkage and low odor, accuracy and dimensional stability, making it perfect for the production of dental models, C&B, thermoforming and aligner models.
Technical specifications
Liqcreate Dental Model Pro Grey is a matte, opaque grey colored photopolymer compatible with open SLA, MSLA and DLP 3D-printers in the range of 385 – 420nm. Its matte surface finish accentuates depth and detail in dental models, which accommodates a perfect view on undercuts and the surface is ideal for scan impressions.
| Mechanical Properties | 30 minutes high power LED curing at 40°C[1] | ||
|---|---|---|---|
| Description | Method | Metric | Imperial |
| Tensile strength | D638 | 49 MPa | 7.1 ksi |
| Tensile modulus | D638 | 2.3 GPa | 334 ksi |
| Elongation at break | D638 | 4.1% | 4.1% |
| Flexural strength | D790 | 89 MPa | 12.9 ksi |
| Flexural modulus | D790 | 2.4 GPa | 348 ksi |
| Shore D hardness | D2240 | 85 | 85 |
| Water sorption | D570-98 | 0.45% | 0.45% |
| Linear shrinkage during printing | Internal method | 0.3% | 0.3% |
| Linear shrinkage during UV-curing | Internal method | 0.4% | 0.4% |
| Degradation temperature | Internal method | 250°C[2] | 482°F[2] |
[1]Post-cured 30 minutes with LED curing at 40°C in the Wicked Engineering Curebox. These values may vary and depend on individual machine processing and post-curing. [2]Discoloration at 160°C, no signs of cracks in post-cured parts up to 250°C / 482°F.
| Description | Value |
|---|---|
| Appearance | Opaque grey liquid |
| Viscosity | 700 cps at 25°C |
| Density | 1.18 g/cm3 |
| Ec (405nm) | 4.62 mJ/cm2 |
| Dp (405nm) | 0.14 mm |
| Ec (385nm) | 2.24 mJ/cm2 |
| Dp (385nm) | 0.07 mm |
| Waga | 1 kg, 6 x 1 kg, 250 gr |
|---|